Solution Annealed Sheet
Temperature
|
Creep
|
Approximate Initial Stress to Produce Specified Creep in
|
10 h
|
100 h
|
1,000 h
|
10,000 h
|
°F
|
°C
|
%
|
ksi
|
MPa
|
ksi
|
MPa
|
ksi
|
MPa
|
ksi
|
MPa
|
1200 |
649 |
0.5 |
- |
- |
- |
- |
46 |
317 |
- |
- |
1 |
- |
- |
- |
- |
53 |
365 |
- |
- |
R |
- |
- |
- |
- |
57 |
393 |
37 |
255 |
1300 |
704 |
0.5 |
- |
- |
45 |
310 |
30 |
207 |
- |
- |
1 |
- |
- |
49 |
338 |
32 |
221 |
- |
- |
R |
- |
- |
51 |
352 |
33 |
228 |
21* |
145* |
1400 |
760 |
0.5 |
38 |
262 |
26 |
179 |
17.5 |
121 |
11.2* |
77* |
1 |
42 |
290 |
29 |
200 |
18.8 |
130 |
11.7 |
81 |
R |
50 |
345 |
33 |
228 |
19.8 |
137 |
12.3 |
85 |
1500 |
816 |
0.5 |
23 |
159 |
15 |
103 |
8.9 |
61 |
- |
- |
1 |
27 |
186 |
16.5 |
114 |
9.9 |
68 |
- |
- |
R |
32 |
221 |
20 |
138 |
11.5 |
79 |
7.0 |
48 |
1600 |
871 |
0.5 |
12.7 |
88 |
7.5 |
52 |
4.5 |
31 |
- |
- |
1 |
15.2 |
105 |
8.7 |
60 |
4.9 |
34 |
- |
- |
R |
21* |
145* |
11.8 |
81 |
6.3 |
43 |
3.4 |
23 |
1700 |
927 |
0.5 |
6.5 |
45 |
3.7 |
26 |
2.1 |
14 |
- |
- |
1 |
7.5 |
52 |
4.2 |
29 |
2.4 |
17 |
- |
- |
R |
9.8 |
68 |
5.6 |
39 |
3.1 |
21 |
1.8* |
12* |
1800 |
982 |
0.5 |
1.9 |
13 |
1.2 |
8.3 |
0.75* |
5.2* |
- |
- |
1 |
2.2 |
15 |
1.3 |
9.0 |
0.83* |
5.7* |
- |
- |
R |
4.8 |
33 |
2.7 |
19 |
1.7 |
12 |
1.0 |
6.9 |
1900 |
1038 |
0.5 |
1.2 |
8.3 |
0.74* |
5.1* |
0.48* |
3.3* |
- |
- |
1 |
1.4 |
10 |
0.88 |
6.1 |
0.55* |
3.8* |
- |
- |
R |
3.3* |
23* |
2.0 |
14 |
1.2 |
8.3 |
0.76 |
5.2 |
2000 |
1093 |
0.5 |
0.75 |
5.2 |
0.55 |
3.8 |
0.32 |
2.2 |
- |
- |
1 |
0.95 |
6.6 |
0.63 |
4.3 |
0.43 |
3.0 |
- |
- |
R |
2.2* |
15* |
1.5 |
10 |
0.94 |
6.5 |
0.61 |
4.2 |
2100 |
1149 |
0.5 |
0.53 |
3.7 |
0.35 |
2.4 |
- |
- |
- |
- |
1 |
0.64 |
4.4 |
0.42 |
2.9 |
0.27 |
1.9 |
- |
- |
R |
1.6* |
11* |
1.1 |
7.6 |
0.69 |
4.8 |
0.44 |
3.0 |
2200 |
1204 |
0.5 |
- |
- |
- |
- |
- |
- |
- |
- |
1 |
- |
- |
- |
- |
- |
- |
- |
- |
R |
1.1* |
7.6* |
0.76 |
5.2 |
0.49 |
3.4 |
- |
- |
*Significant extrapolation
Solution Annealed Plate
Temperature
|
Creep
|
Approximate Initial Stress to Produce Specified Creep in
|
10 h |
100 h |
1,000 h |
10,000 h |
°F
|
°C
|
% |
ksi
|
MPa
|
ksi
|
MPa
|
ksi
|
MPa
|
ksi
|
MPa
|
1400 |
760 |
0.5 |
41* |
283* |
29 |
200 |
21 |
145 |
14* |
97* |
1 |
44* |
303* |
32 |
221 |
23 |
159 |
14.5* |
100* |
R |
55* |
379* |
38 |
262 |
24 |
165 |
15.0 |
103 |
1500 |
816 |
0.5 |
26 |
179 |
19 |
131 |
12.8 |
88 |
7.8* |
54* |
1 |
28 |
193 |
20.5 |
141 |
13.8 |
95 |
8.4* |
58* |
R |
35 |
241 |
23 |
159 |
15.0 |
103 |
9.0* |
62* |
1600 |
871 |
0.5 |
17* |
117* |
11.2 |
77 |
6.2 |
43 |
3.3 |
23 |
1 |
20* |
138* |
12.2 |
84 |
6.7 |
46 |
3.7 |
26 |
R |
24* |
165* |
15.0 |
103 |
8.5 |
59 |
4.6 |
32 |
1700 |
927 |
0.5 |
8.5 |
59 |
4.9 |
34 |
2.6 |
18 |
1.4 |
10 |
1 |
9.7 |
67 |
5.3 |
37 |
2.9 |
20 |
1.6 |
11 |
R |
11.5 |
79 |
7.1 |
49 |
4.2 |
29 |
2.4 |
17 |
1800 |
982 |
0.5 |
2.0 |
14 |
1.3 |
9.0 |
0.85 |
5.9 |
- |
- |
1 |
2.2 |
15 |
1.5 |
10 |
1.00 |
6.9 |
0.68* |
4.7* |
R |
3.9 |
27 |
2.9 |
20 |
1.8 |
12 |
1.1 |
7.6 |
1900 |
1038 |
0.5 |
1.2 |
8.3 |
0.77 |
5.3 |
0.50 |
3.4 |
- |
- |
1 |
1.4 |
10 |
0.91 |
6.3 |
0.60 |
4.1 |
0.39 |
2.7 |
R |
2.9 |
20 |
1.9 |
13 |
1.2 |
8.3 |
0.8 |
5.5 |
2000 |
1093 |
0.5 |
0.77 |
5.3 |
0.48 |
3.3 |
0.29 |
2.0 |
- |
- |
1 |
0.93 |
6.4 |
0.62 |
4.3 |
0.41 |
2.8 |
0.20* |
1.4* |
R |
2.1* |
14* |
1.4 |
9.7 |
0.90 |
6.2 |
0.60 |
4.1 |
2100 |
1149 |
0.5 |
0.47 |
3.2 |
0.27* |
1.9* |
- |
- |
- |
- |
1 |
0.60* |
4.1* |
0.35 |
2.4 |
- |
- |
- |
- |
R |
1.6* |
11* |
1.0 |
6.9 |
0.68 |
4.7 |
0.44 |
3.0 |
2200 |
1204 |
0.5 |
0.35 |
2.4 |
0.19* |
1.3* |
- |
- |
- |
- |
1 |
0.45* |
3.1* |
0.26 |
1.8 |
- |
- |
- |
- |
R |
1.1* |
7.6* |
0.77 |
5.3 |
0.5 |
3.4 |
0.33 |
2.3 |
*Significant extrapolation