Condition |
Test Temperature |
0.2% Yield Strength |
Ultimate Tensile Strength |
4D Elongation |
°F |
°C |
ksi |
MPa |
ksi |
MPa |
% |
Solution Annealed |
RT |
RT |
64.3 |
443 |
128.8 |
888 |
50.1 |
Age Hardened* |
RT |
RT |
129.4 |
892 |
189.9 |
1309 |
24.9 |
1200 |
649 |
114 |
786 |
166.1 |
1145 |
31.8 |
1400 |
760 |
103.7 |
715 |
119.6 |
825 |
34.5 |
1500 |
816 |
75.9 |
523 |
92.1 |
635 |
40.6 |
1600 |
871 |
52.6 |
363 |
66.9 |
461 |
45.7 |
Age Hardened* + 1200°F/8000h |
RT |
RT |
137.8 |
950 |
197 |
1358 |
21.8 |
1200 |
649 |
120.7 |
832 |
171.3 |
1181 |
29.7 |
Age Hardened* + 1400°F/8000h |
RT |
RT |
115.2 |
794 |
178.2 |
1229 |
19 |
1400 |
760 |
80.2 |
553 |
110.3 |
760 |
32.1 |
Age Hardened* + 1500°F/8000h |
RT |
RT |
93.2 |
643 |
160.4 |
1106 |
22.2 |
1500 |
816 |
51.1 |
352 |
79.9 |
551 |
31.3 |
Age Hardened* + 1600°F/8000h |
RT |
RT |
66 |
455 |
115.7 |
798 |
13 |
1600 |
871 |
30.5 |
210 |
49.9 |
344 |
29.2 |
*Samples were age hardened by treating at 1825°F (995°C)/2 Hr./AC + 1550°F (845°C)/4 Hr./AC + 1400°F (760°C)/16 Hr./AC